成果简介：Mesoporous TiO2 coated SBA-15 (MT@S) nanocomposites were fabricated through supercritical CO2 deposition aided by liquid-crystal template. MT uniformly deposited onto silica with titania incorporated in SBA-15 channels, showed smaller crystallite size, higher hydroxyl content and surface area than nonporous TiO2 coated SBA-15 (NT@S) obtained by a similar route without template. With TiO2 loading ratio of 15wt% and calcination temperature of 400 °C, 15%MT@S-400 showed the enhanced degradation efficiency for azo dyes (methylene blue, methyl orange, and rhodamine B) and phenol in comparsion with 15%NT@S-400, due to those improved textural and physicochemical properties. Meanwhile, the reused MT@S also showed high photoactivity. Additionally, the effects of MT content and calcination temperature have been examined as operational parameters. Photocatalytic reactions followed pseudo-first-order kinetics and are discussed in terms of the Langmuir–Hinshelwood model.

论文引用方式：Chen Liu, Xiao Lin, Youji Li, Peng Xu, Ming Li, Feitai Chen. Enhanced photocatalytic performance of mesoporous TiO2 coated SBA-15 nanocomposites fabricated through a novel approach: supercritical deposition aided by liquid-crystal template.Materials Research Bulletin, 75, 2016, 25-34

论文链接：http://www.sciencedirect.com/science/article/pii/S0025540815301872