成果简介：Monoclinic Li3V2-xWx(PO4)3/C (x=0, 0.03,0.05,0.07,0.10) compounds were successfully synthesized by the sol-gel method. X - ray diffraction (XRD) patterns demonstrated that the appropriate addition of tungsten enlarged the unit cell volume of Li3V2(PO4)3, which could provide more space for lithium intercalation/deintercalation. The Xray photoelectron spectroscopy (XPS) analysis revealed that the main chemical state of VintheLi3V1.93W0.07(PO4)3/C compositeis +3 valence, while the chemical state of W in the Li3V1.93W0.07(PO4)3/C is +5 valence. Scanning electronmicroscope (SEM) analyses illustrated that the addition of W slightly affected the morphology of samples. Li3V2 xWx(PO4)3/C (x≤0.10) exhibited higher discharge capacity and better cycle stability than the pure one. For the optimal composition of Li3V1.93W0.07(PO4)3/C, the initial discharge capacity was 160.3 mAhg1 and 95.5% capacity retention was observed after 50 cycles at 0.5 C rate. Cyclic voltammetry (CV) result revealed the reversibility was enhanced after V3+ substituted by W5+. The enhanced electrochemical performances can be attributed to the smaller particle size, higher surface area and enhanced structural stability during the proper amount of W doping in V sites.

论文引用方式：Ao Xia, Jianfeng Huang, Guoqiang Tan, Huijun Ren. Synthesis and electrochemical properties of W-doped Li3V2(PO4)3/C cathode materials for lithiumion batteries. Ceramics International, 2014, 40,14845-14850.

论文链接：http://www.sciencedirect.com/science/article/pii/S0272884214009730